Magnesia Alumina Spinel Brick
Magnesia alumina spinel bricks can be used in the cement kiln, not only avoid the chrome pollution, and has good anti-stripping performance.
- MgO: 82-88%
- Al2O3: 6-9%
- Bulk Density: 2.8-2.9g/cm3
- Long service life
- Environment friendly
- For transition zone of cement kilns
Product Details
Magnesia alumina spinel brick is a kind of alkaline refractory product with periclase as main phase and magnesia-alumina spinel clinker as basic material. The product is of good temperature vibration, good strength and volume stability in high temperature environment.
| Iterms | KRSH-1 | KRSH-2 | KRSH-3 | KRSH-4 |
| МgО％, ≥ | 88 | 86 | 84 | 82 |
| Аl2О3％, ≥ | 6 | 9 | 9 | 8 |
| SiО2％, ≥ | 0,5 | 0,5 | 0,8 | 1,0 |
| Bulk density, g/cm3 | 2.9 | 2.9 | 2.85 | 2.8 |
| Open porosity,%, ≤ | 18 | 18 | 19 | 20 |
| Compressive strength, N/mm², ≥ | 60 | 60 | 50 | 45 |
| Softening onset temperature, ℃, ≥ | 1700 | 1700 | 1680 | 1650 |
| Thermal resistance, ≥, times | 10 | 10 | 10 | 10 |
| Thermal conductivity, 1000℃, W/m K | 2.9 | 2.9 | 2.8 | 2.7 |
Application:
- The magnesia alumina spinel bricks can be used in the cement kiln, not only avoid the chrome pollution, and has good anti-stripping performance.
- It can be used in refractory carstables for ladles, which greatly improve the anti-erosion ability. It is widely applied to steel-making refractory material. The preparation of high quality pre-synthertic spinel provide a new material for amorphous and fixed high purity refractory.